Mae cynhyrchion Bar Rownd Titaniwm yn unol ag ASTM B348 / ASME SB348 ar gael yn Graddau 1, 2, 3, 4, Ti6AL4V a graddau titaniwm eraill mewn meintiau hyd at ddieeter 500mm.
Mae meintiau petryal a sgwâr hefyd ar gael.
Rydym yn cyflenwi graddau awyrofod
fel AMS 4928, AMS 4911, AMS 2631, AMS 4901, AMS 4907, AMS 4919, AMS 6931, AMS T 9046, AMS T 9047 a
safonau rhyngwladol
fel ASTM B 337, ASTM B 338, ASTM B 381, ASTM F 67, ASTM F 136, ASTM B348, ASTM B265 a
pibellau, ffitiadau & flanges gyda
NORSOK M630 Rev 2 MDS T01 manylebau am brisiau titaniwm cystadleuol iawn.
Disgrifiad
Rhennir bar titaniwm yn far titaniwm pur a bariau aloi titaniwm. Ar gyfer bariau titaniwm pur rydym yn darparu Graddau Gr1, Gr2, Gr4 a graddau eraill yn bennaf; rydym yn darparu bariau aloi titaniwm o Gr5, Gr7, Gr9, Gr11, Gr12, Gr16, Gr23 ac ati.
Bar titaniwm yw un o'r mathau mwyaf cyffredin o gynhyrchion titaniwm. Mae'n ddeunydd sylfaenol llawer o gynhyrchion titaniwm i'w prosesu ymhellach. Gellir cynhyrchu'r bar titaniwm diamedr mwy yn uniongyrchol trwy ffugio. Mae gennym yr offer maddau am ddim sy'n helpu i gynhyrchu'r bariau titaniwm maint mawr. Yn y broses o greu, mae'r ingot titaniwm yn cael ei ddadffurfio'n unffurf mewn amser byr o'r tu mewn i'r tu allan, wedi gwella priodweddau mecanyddol y titaniwm. Mae'r ansawdd materol wedi gwella'n fawr o'i gymharu â'r maddeuant morthwyl; Gellir cynhyrchu bariau titaniwm diamedr bach ar ôl rholio ac atodi lluosog, a thynnu haen ocsid titaniwm drwy brosesu mecanyddol yn y pen draw.
Rydym yn darparu arwyneb troi ac arwyneb caboledig o far titaniwm. Ar yr un pryd, mae gennym ddigon o ddyfeisiau bariau titaniwm mewn gwahanol feintiau, ar gyfer y cwsmeriaid hynny sydd â galwadau brys ar yr adeg cyflwyno a'r cwsmeriaid sydd â swm bach sydd ei angen.
UNS Rhif
| UNS Rhif | UNS Rhif | ||||
| Gr1 | UNS R50250 | CP-Ti | Gr11 | UNS R52250 | Ti-0.15Pd |
| Gr2 | UNS R50400 | CP-Ti | Gr12 | UNS R53400 | Ti-0.3Mo-0.8Ni |
| Gr4 | UNS R50700 | CP-Ti | Gr16 | UNS R52402 | Ti-0.05Pd |
| Gr7 | UNS R52400 | Ti-0.20Pd | Gr23 | UNS R56407 | Ti-6Al-4V ELI |
| Gr9 | UNS R56320 | Ti-3Al-2.5V | |||
Manylebau
| Gradd | Statws | Diamedr(mm) | Hyd(mm) |
| Gr1,Gr2,Gr4,Gr5,Gr7,Gr9,Gr11,Gr12,Gr16,Gr23 | Wedi'i rolio'n boeth (R) | 6 ~ 115 | 10 ~ 6000 |
| Wedi'i rolio'n oer (Y) | |||
| Annealed (M) |
Cyfansoddiad cemegol
| Gradd | Cyfansoddiad cemegol, pwysau y cant (%) | ||||||||||||
| C (≤) | O (≤) | N (≤) | H (≤) | Ab (≤) | Al | V | Pd | Ru | Ni | Mo | Elfennau Eraill Max. pob un | Elfennau Eraill Max. cyfanswm | |
| Gr1 | 0.08 | 0.18 | 0.03 | 0.015 | 0.20 | — | — | — | — | — | — | 0.1 | 0.4 |
| Gr2 | 0.08 | 0.25 | 0.03 | 0.015 | 0.30 | — | — | — | — | — | — | 0.1 | 0.4 |
| Gr4 | 0.08 | 0.25 | 0.03 | 0.015 | 0.30 | — | — | — | — | — | — | 0.1 | 0.4 |
| Gr5 | 0.08 | 0.20 | 0.05 | 0.015 | 0.40 | 5.5 ~ 6.75 | 3.5 ~ 4.5 | — | — | — | — | 0.1 | 0.4 |
| Gr7 | 0.08 | 0.25 | 0.03 | 0.015 | 0.30 | — | — | 0.12 ~ 0.25 | — | 0.12 ~ 0.25 | — | 0.1 | 0.4 |
| Gr9 | 0.08 | 0.15 | 0.03 | 0.015 | 0.25 | 2.5 ~ 3.5 | 2.0 ~ 3.0 | — | — | — | — | 0.1 | 0.4 |
| Gr11 | 0.08 | 0.18 | 0.03 | 0.15 | 0.2 | — | — | 0.12 ~ 0.25 | — | — | — | 0.1 | 0.4 |
| Gr12 | 0.08 | 0.25 | 0.03 | 0.15 | 0.3 | — | — | — | — | 0.6 ~ 0.9 | 0.2 ~ 0.4 | 0.1 | 0.4 |
| Gr16 | 0.08 | 0.25 | 0.03 | 0.15 | 0.3 | — | — | 0.04 ~ 0.08 | — | — | — | 0.1 | 0.4 |
| Gr23 | 0.08 | 0.13 | 0.03 | 0.125 | 0.25 | 5.5 ~ 6.5 | 3.5 ~ 4.5 | — | — | — | — | 0.1 | 0.1 |
Priodweddau ffisegol
| Gradd | Priodweddau ffisegol | |||||
| Cryfder tynnol Munud | Cryfder y cynnyrch Min (0.2%,offset) | Huawdl mewn 4D Min (%) | Lleihau Arwynebedd Min (%) | |||
| ksi | Mpa | ksi | Mpa | |||
| Gr1 | 35 | 240 | 20 | 138 | 24 | 30 |
| Gr2 | 50 | 345 | 40 | 275 | 20 | 30 |
| Gr4 | 80 | 550 | 70 | 483 | 15 | 25 |
| Gr5 | 130 | 895 | 120 | 828 | 10 | 25 |
| Gr7 | 50 | 345 | 40 | 275 | 20 | 30 |
| Gr9 | 90 | 620 | 70 | 483 | 15 | 25 |
| Gr11 | 35 | 240 | 20 | 138 | 24 | 30 |
| Gr12 | 70 | 483 | 50 | 345 | 18 | 25 |
| Gr16 | 50 | 345 | 40 | 275 | 20 | 30 |
| Gr23 | 120 | 828 | 110 | 759 | 10 | 15 |
Goddefgarwch (mm)
| Diamedr | Amrywiadau maint | Allan o rownd, Allan o sgwâr |
| 6.0 ~ 8.0 | ±0.13 | 0.20 |
| 8.0 ~ 11.0 | ±0.15 | 0.23 |
| 11.0 ~ 16.0 | ±0.18 | 0.25 |
| 16.0 ~ 22.0 | ±0.20 | 0.30 |
| 22.0 ~ 25.0 | ±0.23 | 0.33 |
| 25.0 ~ 28.0 | ±0.25 | 0.38 |
| 28.0 ~ 32.0 | ±0.28 | 0.41 |
| 32.0 ~ 35.0 | ±0.30 | 0.46 |
| 35.0 ~ 38.0 | ±0.36 | 0.53 |
| 38.0 ~ 50.0 | ±0.40 | 0.58 |
| 50.0 ~ 65.0 | +0.79 | 0.58 |
| 65.0 ~ 90.0 | +1.19 | 0.89 |
| 90.0 ~ 115.0 | +1.59 | 1.17 |
Gallwn ddarparu bar crwn, bar sgwâr, bar hecsagonol, wyth bar sgwâr, bar gwastad ac ati.
Profi
Prawf cyfansoddiad cemegol
Prawf priodweddau ffisegol
Arolygiad diffygion ymddangosiad
Canfod fflaw uwchsain
Profion cyfredol Eddy
Deunydd pacio
Er mwyn osgoi'r bariau titaniwm, mae unrhyw wrthdrawiad wrth ei gludo neu ei ddifrodi, fel arfer wedi'i lapio â cotwm perlog (polyethylen y gellir ei ehangu), ac yna'n cael ei bacio'n achos pren i'w gyflwyno.
Tagiau poblogaidd: astm b348 gradd 5 titaniwm rownd bar, Tsieina, gweithgynhyrchwyr, cyflenwyr, ffatri